Diving into Exploration

Flickr’s Dragonfly555 shows off impressions samples.

Do you feel like you have to make a finished piece or be working on a particular design when you sit down at your studio table? Sure, it feels good, and it’s very exciting to have a finished piece to show and share, but learning a craft is as much about exploration as is about creating finished work.

So, if you’re not giving yourself that exploratory time, let me give you some reasons to highly consider it. And if you do a bit of exploring already, maybe I can offer up some new ideas about ways to use and organize your exploratory bits that you might not have tried.

 

The Exploratory Reasoning

When you’re fairly new to a material, technique, form, or construction method, it is to your advantage to spend time just playing with it. This is especially true, I think, of texture, mark making, color mixing, new techniques, and new materials including new brands of a familiar material. Trying to make finished work before you are familiar with the technique or material can get frustrating, if not downright depressing. You can gain more success in the long run if you develop a better understanding of what it is that you’re working and hone your skills a bit before gambling your time, materials, and hopes on finished work.

It certainly can be tempting to just pick up something and see what you can make with it right out the gate. With a lot of home craft materials, polymer clay in particular, you can create a decent completed piece within a day of picking it up. However, the ease of these materials is a bit of a deception. They may be easy to get started with, but mastering them, even just a little, takes time and effort. Give yourself a gift of that time to get to know what you’re working with without the pressure of trying to finish something presentable.

 

Samples to Reference

Mica powders with sample chips

Probably the best way to explore new materials and techniques is to make small samples, ones you can keep and reference as you make decisions for future finished pieces. If the color of the sample is not relevant, you can just use scrap clay. If you use clay straight out of the package, you may also have an option to transform the samples into finished work. Let’s go over all these options.

(Although I’m going to talk specifically about polymer clay, if you work primarily in another material, consider an equivalent process. Consider how you can cut out or form small samples that can be saved as references. See if this clay focused process inspires you.)

For some orderly exploration, sheet your clay and then hand cut or punch cut the sheets into whatever shapes tickle your fancy. Then you can just go crazy with whatever you’re exploring. Use as many of these pieces as you like for each process you’re exploring. Keep the ones you are pleased with, etching with a needle tool or, after curing, writing on the back with permanent marker, what you made them with. Keep cured pieces in a baggie or punch holes in them before curing so you can string them on wire or chain, making them easy to flip through.

If you are playing with textures, mark making, or any kind of tooling on polymer clay, I would suggest sheeting three different thicknesses—the thickest setting, a medium setting, and the thinnest setting on your pasta machine. Then try out each of your experiments at least once on each of the three different thicknesses. Anything that impresses or otherwise moves around the clay will be affected differently by the clay thickness, sometimes subtly but sometimes quite dramatically.

Cure the samples you like, being sure to inscribe or write a note on the back indicating what thickness the clay sheet was along with what made the impression or marks.

If you’re color mixing, sheet the finished color, then punch out a decent sized shape, one that has enough room for you to write down your proportions for that color mix. For example, if you mix a deep rich purple by combining 6 parts cobalt, 3 parts magenta, and one part black, inscribe on the back:

6X blue

3X magenta

1X black

Also include a big initial for the brand of clay (P for Premo, F for Fimo, K for Kato, etc) since colors by the same name in one brand are usually nothing like those colors in another brand.

You can also note proportions visually by punching out a circle of clay, smaller than your mixed sample, from each of the colors you used in the mix. Cut out portions, like pie slices, from each color in proportion to how much was used in the mix to re-create a single circle showing how much of each color was used in the mix. Don’t forget to inscribe your initial for the brand of clay. See the image here for an approximate example of the purple mix above.

Adhere this combination pie to the mixed color shape, punch a hole in the sample, cure, and string on a chain or wire.

(If you are confused about how to figure out the parts aspect of the color mixing, just use a small cutter to punch your unmixed colors out of sheets of the same thickness. Each piece is a part. Use these punched bits of clay to make your mix, keeping track of how many pieces/parts you use to create the color you’re making.)

If you’re playing with a surface colorant, try it on both white clay and black clay or on clay colors you use quite often. It’s a rare colorant that doesn’t allow the clay base underneath to the show through, so trying it on black and white will give you an idea of how the colorant will appear on lighter versus darker colors, not just black and white.

I punch small-ish circles out of white and black sheets of clay, then I cut them in half and put a white half with a black half. I apply the colorant to these splits chips. After curing, I glue them to the colorant’s product container so my reference sample is right on the product. You can see here how well this works for those little mica powder containers, above. I keep them in a drawer with the samples facing up so I can quickly find the color I want.

The best part about all these samples is that while you’re designing a finished piece, you can pull them out and compare them side-by-side to see what works well together. You can also hold them up to a partially finished piece to see what you might want to add. Personally, I can’t imagine working without all my exploratory samples.

 

Turning Discovery into Works of Art

Just a few pendants and beads I made with extra texture samples by reforming and/or adding pin lace layers of clay. You can learn the pin lace technique in the February VAB here. The VAB PDFs are 40% right now too.

Now, for those of you who are anxious to produce something with your time at the studio table, you can take any samples you’re not going to save for reference and create with them. You can add additional layers, reshape, or attach embellishment to your extra samples to easily create pendants, earrings, or brooches. You can also use them for collages or mosaics.

Keep cured samples, even if you’re not going to use them for reference, for further experiments where you want to play with cured clay techniques or to test new glues or sealants. This way, not only is your time not wasted, neither are any of the materials you’re playing with.

 

Give Yourself Permission to Explore

Whatever your inclination, the big take-away here is that in-depth exploration can, and probably should, be a regular part of your creative process. Give yourself the permission and time to do this throughout your creative journey or career, not just when you’re starting out.

Keep in mind, not only does this kind of exploratory time hone your skills, your familiarity and confidence with the processes and techniques grow stronger and faster than they would if you tried to learn just through making finished work. This is because you are willing to take more chances with these scrap samples. They just don’t have the same stakes, right?

And, you know, taking chances with this exploratory sample work should eventually translate into taking bigger risks with your finished pieces. I think, when we take the big risks, that’s when we make the biggest leaps and create the most amazing work. Well, sometimes we make absolute disasters as well, but it’s all part of the process. You’re certainly less likely to have a disaster if you do a lot of exploration first.

Christi Friesen shares unusual and creative mark making in the March Virtual Art Box

So, if you have not let yourself just explore and play with the materials you work with, maybe, this week, you can either set some time aside or make all of your studio time exploration time. Making many of your mistakes in the exploratory phase and not always on completed pieces will make your creative time more efficient, less stressful, and more enjoyable.

 

Texture Hungry?

If you’re one of those who is looking for more ideas and direction on texture, don’t forget we have an entire issue of The Polymer Arts on texture, the Fall 2017 issue. Also check out the mark making focused edition of the Virtual Art Box from March of last year. All Virtual Art Box content that was previously members only is 40% off right now.

 

 

The Last of the March Giveaways

Our month of giveaways has ended, but all your wonderful comments have given me so many ideas for upcoming posts. I thank all of you who commented so very sincerely!

I have one last giveaway winner to announce. Valerie Hall is receiving the last batch of my giveaway Polyform clay. I was very excited about this. Valerie is a very active and giving soul who has been trying to teaching through the great clay shortage of 2020 in any way she can. So it’s fantastic to aid her with this clay package. Congrats Valerie!

This was so much fun. I will try to do this here and there as I receive samples or find opportunities to gather stuff for you. So stick around for more free stuff in the not-too-distant future!


 

You can support this blog by buying yourself a little something at Tenth Muse Arts or, if you like…


 

The Journey of The Broken Telephone

For those of you who followed the blogging I did from Synergy, you may remember Dan Cormier’s Broken Telephone Project. We couldn’t reveal much then because Dan and partner Tracy were going to roll out the series on The Cutting Edge Facebook page and who was I to spoil the surprise.

Well Dan has now revealed all the beautiful brooches, their creators and his thoughts on the project and related subjects. The conversation he’s started on his wrap-up post (posted on both Facebook and Flickr) is very important and I would encourage you all to take a minute to read it.

While there, take a look at all the gorgeous pieces that came out of the project.

539877_384069808367379_86934425_n

I was lucky enough to get a close-up look of each of these brooches as I helped pin them on Tracy who became a walking exhibition on the last night of Synergy 3. I’ve held back photos of this unique exhibit until the roll-out was complete. Tracy was easily the best adorned lady of the evening!

_DSC0586

_DSC0584

Real Leaves, Real Easy

The leaves in the brooches below look deceptively real.  For good reason. They are the result of direct impressions from real leaves. That and a little paint to bring out the veins. It doesn’t get much more real than that. Except for the real thing of course.

The clay used by artist Camille Young here is actually Lumina. It’s a translucent polymer resin clay that air dries. You color it with acrylic or oil based paints. But, this is just as easy to replicate in polymer and there’s no mixing in of paint into the clay. Choose a leaf color or skinner blend a few colors of clay together, then press in a real leaf, bake, apply acrylic paint to get it into the veins and then wipe off the paint on the raised surface.

Camille documents her creation of these leaves in Lumina on her blog here (scroll down when you get to the page … she has a large header). Just follow the steps except bake the polymer where she says “let it dry thoroughly”.

Grand idea!

Diving into Exploration

April 4, 2021
Posted in ,

Flickr’s Dragonfly555 shows off impressions samples.

Do you feel like you have to make a finished piece or be working on a particular design when you sit down at your studio table? Sure, it feels good, and it’s very exciting to have a finished piece to show and share, but learning a craft is as much about exploration as is about creating finished work.

So, if you’re not giving yourself that exploratory time, let me give you some reasons to highly consider it. And if you do a bit of exploring already, maybe I can offer up some new ideas about ways to use and organize your exploratory bits that you might not have tried.

 

The Exploratory Reasoning

When you’re fairly new to a material, technique, form, or construction method, it is to your advantage to spend time just playing with it. This is especially true, I think, of texture, mark making, color mixing, new techniques, and new materials including new brands of a familiar material. Trying to make finished work before you are familiar with the technique or material can get frustrating, if not downright depressing. You can gain more success in the long run if you develop a better understanding of what it is that you’re working and hone your skills a bit before gambling your time, materials, and hopes on finished work.

It certainly can be tempting to just pick up something and see what you can make with it right out the gate. With a lot of home craft materials, polymer clay in particular, you can create a decent completed piece within a day of picking it up. However, the ease of these materials is a bit of a deception. They may be easy to get started with, but mastering them, even just a little, takes time and effort. Give yourself a gift of that time to get to know what you’re working with without the pressure of trying to finish something presentable.

 

Samples to Reference

Mica powders with sample chips

Probably the best way to explore new materials and techniques is to make small samples, ones you can keep and reference as you make decisions for future finished pieces. If the color of the sample is not relevant, you can just use scrap clay. If you use clay straight out of the package, you may also have an option to transform the samples into finished work. Let’s go over all these options.

(Although I’m going to talk specifically about polymer clay, if you work primarily in another material, consider an equivalent process. Consider how you can cut out or form small samples that can be saved as references. See if this clay focused process inspires you.)

For some orderly exploration, sheet your clay and then hand cut or punch cut the sheets into whatever shapes tickle your fancy. Then you can just go crazy with whatever you’re exploring. Use as many of these pieces as you like for each process you’re exploring. Keep the ones you are pleased with, etching with a needle tool or, after curing, writing on the back with permanent marker, what you made them with. Keep cured pieces in a baggie or punch holes in them before curing so you can string them on wire or chain, making them easy to flip through.

If you are playing with textures, mark making, or any kind of tooling on polymer clay, I would suggest sheeting three different thicknesses—the thickest setting, a medium setting, and the thinnest setting on your pasta machine. Then try out each of your experiments at least once on each of the three different thicknesses. Anything that impresses or otherwise moves around the clay will be affected differently by the clay thickness, sometimes subtly but sometimes quite dramatically.

Cure the samples you like, being sure to inscribe or write a note on the back indicating what thickness the clay sheet was along with what made the impression or marks.

If you’re color mixing, sheet the finished color, then punch out a decent sized shape, one that has enough room for you to write down your proportions for that color mix. For example, if you mix a deep rich purple by combining 6 parts cobalt, 3 parts magenta, and one part black, inscribe on the back:

6X blue

3X magenta

1X black

Also include a big initial for the brand of clay (P for Premo, F for Fimo, K for Kato, etc) since colors by the same name in one brand are usually nothing like those colors in another brand.

You can also note proportions visually by punching out a circle of clay, smaller than your mixed sample, from each of the colors you used in the mix. Cut out portions, like pie slices, from each color in proportion to how much was used in the mix to re-create a single circle showing how much of each color was used in the mix. Don’t forget to inscribe your initial for the brand of clay. See the image here for an approximate example of the purple mix above.

Adhere this combination pie to the mixed color shape, punch a hole in the sample, cure, and string on a chain or wire.

(If you are confused about how to figure out the parts aspect of the color mixing, just use a small cutter to punch your unmixed colors out of sheets of the same thickness. Each piece is a part. Use these punched bits of clay to make your mix, keeping track of how many pieces/parts you use to create the color you’re making.)

If you’re playing with a surface colorant, try it on both white clay and black clay or on clay colors you use quite often. It’s a rare colorant that doesn’t allow the clay base underneath to the show through, so trying it on black and white will give you an idea of how the colorant will appear on lighter versus darker colors, not just black and white.

I punch small-ish circles out of white and black sheets of clay, then I cut them in half and put a white half with a black half. I apply the colorant to these splits chips. After curing, I glue them to the colorant’s product container so my reference sample is right on the product. You can see here how well this works for those little mica powder containers, above. I keep them in a drawer with the samples facing up so I can quickly find the color I want.

The best part about all these samples is that while you’re designing a finished piece, you can pull them out and compare them side-by-side to see what works well together. You can also hold them up to a partially finished piece to see what you might want to add. Personally, I can’t imagine working without all my exploratory samples.

 

Turning Discovery into Works of Art

Just a few pendants and beads I made with extra texture samples by reforming and/or adding pin lace layers of clay. You can learn the pin lace technique in the February VAB here. The VAB PDFs are 40% right now too.

Now, for those of you who are anxious to produce something with your time at the studio table, you can take any samples you’re not going to save for reference and create with them. You can add additional layers, reshape, or attach embellishment to your extra samples to easily create pendants, earrings, or brooches. You can also use them for collages or mosaics.

Keep cured samples, even if you’re not going to use them for reference, for further experiments where you want to play with cured clay techniques or to test new glues or sealants. This way, not only is your time not wasted, neither are any of the materials you’re playing with.

 

Give Yourself Permission to Explore

Whatever your inclination, the big take-away here is that in-depth exploration can, and probably should, be a regular part of your creative process. Give yourself the permission and time to do this throughout your creative journey or career, not just when you’re starting out.

Keep in mind, not only does this kind of exploratory time hone your skills, your familiarity and confidence with the processes and techniques grow stronger and faster than they would if you tried to learn just through making finished work. This is because you are willing to take more chances with these scrap samples. They just don’t have the same stakes, right?

And, you know, taking chances with this exploratory sample work should eventually translate into taking bigger risks with your finished pieces. I think, when we take the big risks, that’s when we make the biggest leaps and create the most amazing work. Well, sometimes we make absolute disasters as well, but it’s all part of the process. You’re certainly less likely to have a disaster if you do a lot of exploration first.

Christi Friesen shares unusual and creative mark making in the March Virtual Art Box

So, if you have not let yourself just explore and play with the materials you work with, maybe, this week, you can either set some time aside or make all of your studio time exploration time. Making many of your mistakes in the exploratory phase and not always on completed pieces will make your creative time more efficient, less stressful, and more enjoyable.

 

Texture Hungry?

If you’re one of those who is looking for more ideas and direction on texture, don’t forget we have an entire issue of The Polymer Arts on texture, the Fall 2017 issue. Also check out the mark making focused edition of the Virtual Art Box from March of last year. All Virtual Art Box content that was previously members only is 40% off right now.

 

 

The Last of the March Giveaways

Our month of giveaways has ended, but all your wonderful comments have given me so many ideas for upcoming posts. I thank all of you who commented so very sincerely!

I have one last giveaway winner to announce. Valerie Hall is receiving the last batch of my giveaway Polyform clay. I was very excited about this. Valerie is a very active and giving soul who has been trying to teaching through the great clay shortage of 2020 in any way she can. So it’s fantastic to aid her with this clay package. Congrats Valerie!

This was so much fun. I will try to do this here and there as I receive samples or find opportunities to gather stuff for you. So stick around for more free stuff in the not-too-distant future!


 

You can support this blog by buying yourself a little something at Tenth Muse Arts or, if you like…


 

Read More

The Journey of The Broken Telephone

April 6, 2013
Posted in ,

For those of you who followed the blogging I did from Synergy, you may remember Dan Cormier’s Broken Telephone Project. We couldn’t reveal much then because Dan and partner Tracy were going to roll out the series on The Cutting Edge Facebook page and who was I to spoil the surprise.

Well Dan has now revealed all the beautiful brooches, their creators and his thoughts on the project and related subjects. The conversation he’s started on his wrap-up post (posted on both Facebook and Flickr) is very important and I would encourage you all to take a minute to read it.

While there, take a look at all the gorgeous pieces that came out of the project.

539877_384069808367379_86934425_n

I was lucky enough to get a close-up look of each of these brooches as I helped pin them on Tracy who became a walking exhibition on the last night of Synergy 3. I’ve held back photos of this unique exhibit until the roll-out was complete. Tracy was easily the best adorned lady of the evening!

_DSC0586

_DSC0584

Read More

Real Leaves, Real Easy

November 20, 2012
Posted in ,

The leaves in the brooches below look deceptively real.  For good reason. They are the result of direct impressions from real leaves. That and a little paint to bring out the veins. It doesn’t get much more real than that. Except for the real thing of course.

The clay used by artist Camille Young here is actually Lumina. It’s a translucent polymer resin clay that air dries. You color it with acrylic or oil based paints. But, this is just as easy to replicate in polymer and there’s no mixing in of paint into the clay. Choose a leaf color or skinner blend a few colors of clay together, then press in a real leaf, bake, apply acrylic paint to get it into the veins and then wipe off the paint on the raised surface.

Camille documents her creation of these leaves in Lumina on her blog here (scroll down when you get to the page … she has a large header). Just follow the steps except bake the polymer where she says “let it dry thoroughly”.

Grand idea!

Read More